Silindirler PU çubuğu yapmak için ptmeg tabanlı prepolimer
Son Fiyat alınÖdeme şekli: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. sipariş: | 1000 Kilogram |
Ulaşım: | Ocean |
Liman: | Shanghai |
Ödeme şekli: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Min. sipariş: | 1000 Kilogram |
Ulaşım: | Ocean |
Liman: | Shanghai |
model numarası.: XCPU-M135
Marka: Xuchuan kimyasal
Place Of Origin: China
Types Of: Synthetic Resin And Plastics
Appearance: solid
Features: Water resistance, low temperature resistance, mildew resistance
Application: Typical uses of this polymer include forklift truck tyres, rolls, and gears, die pads etc
Brand: Xuchuan
Xuchuan Chemical (Suzhou) Co., Ltd, ayakkabı tabanı için PU sistemi, ayakkabılar için yapıştırıcı, TPU, CPU, polyester poliol, mürekkep için PU reçinesi, pur sıcak eriyik yapıştırıcısı, esnek paket için yapıştırıcı, Sentetik için PU reçinesidir. Deri.
Poliether (PTMEG) TDI prepolimer XCPU-M135
Name of products
|
Appearances
|
Viscosity(mPa.s/85℃)
|
NCO% content
|
Package(kg)
|
XCPU-M135
|
solid
|
1200-1300
|
3.50-3.70
|
20 / 200
|
5、Mixing and Curing Conditions
|
|
|
|
|
|
|
||||||
MOCA Level
|
Recommended % Theory
|
Prepolymer Temperature
|
Curative Temperature
|
Pot Life
|
Demould Time
|
Post Cure Time
|
||||||
%
|
%
|
℃
|
℃
|
mins
|
@ 100°C (hrs)
|
@ 100°C (hrs)
|
||||||
10.5
|
95
|
75-85
|
110-120
|
11-12
|
1
|
10
|
Hardness
|
Shore A
|
85
|
Tensile Strength
|
MPa
|
27
|
100% Modulus
|
MPa
|
5.4
|
300% Modulus
|
MPa
|
9.6
|
Angle Tear Strength, Die C
|
kN/m
|
65
|
Trouser Tear Strength
|
kN/m
|
21
|
Elongation
|
%
|
550
|
Resilience
|
%
|
61
|
DIN Abrasion Resistance 10N
|
mm 3
|
39
|
Cured Specific Gravity
|
g/cm3
|
1.07
|
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.